KWFG02
Kewei
| Quantity: | |
|---|---|
Specifications:
| Technical Date of Fiberglass Duct Rodd | ||
| Specification
| Rod Diameter (mm) | 6mm |
| Rod Length (m) | 100m | |
|
Material
| Fiberglass rod inner | Extruded by fiber glass and high strength resin at high temperature |
| Fiber glass rod outer | High Density polyethylene coating | |
| Metal Frame | Steel with high-temperature sprayed plastic or hot dip galvanized | |
| Physical Property | Fiber glass content | 75-80% |
| Density | > 1.9gr/cm3 | |
| Working environment | -40° C to +80° C | |
| Minimum Pulling strength
| 4000N +/-5% | |
| Consistency of rod | 137gr/m | |
| Flexural Modulus | > 46.500Mpa | |
| Elongation at break | 2.5-3% | |
| Min Bending Radius | 388mm | |
Technical Data:
| Specification(dia. mm) | Max. tensile strength(KN) | Max. bending force(KN) |
| 4.5 | --- | 0.205 |
| 6 | --- | 0.396 |
| 8 | 2.67 | 0.825 |
| 9 | 19.66 | 1.18 |
| 11 | 19.66 | 1.18 |
| 14 | 25.36 | 1.76 |
| 16 | 29.54 | 2.85 |
Specifications:
| Technical Date of Fiberglass Duct Rodd | ||
| Specification
| Rod Diameter (mm) | 6mm |
| Rod Length (m) | 100m | |
|
Material
| Fiberglass rod inner | Extruded by fiber glass and high strength resin at high temperature |
| Fiber glass rod outer | High Density polyethylene coating | |
| Metal Frame | Steel with high-temperature sprayed plastic or hot dip galvanized | |
| Physical Property | Fiber glass content | 75-80% |
| Density | > 1.9gr/cm3 | |
| Working environment | -40° C to +80° C | |
| Minimum Pulling strength
| 4000N +/-5% | |
| Consistency of rod | 137gr/m | |
| Flexural Modulus | > 46.500Mpa | |
| Elongation at break | 2.5-3% | |
| Min Bending Radius | 388mm | |
Technical Data:
| Specification(dia. mm) | Max. tensile strength(KN) | Max. bending force(KN) |
| 4.5 | --- | 0.205 |
| 6 | --- | 0.396 |
| 8 | 2.67 | 0.825 |
| 9 | 19.66 | 1.18 |
| 11 | 19.66 | 1.18 |
| 14 | 25.36 | 1.76 |
| 16 | 29.54 | 2.85 |